Die Casting Porosity Causes and Solutions - Part 3

Posted by Hill and Griffith Company on Apr 26, 2018 11:05:03 AM

By Tim Cowell, Hill and Griffith Company, Technical Director

Gas Porosity (Lubricant)

The lubricant used on the dies or on the plunger can generate gas when heated by the incoming metal. This gas (like the steam) is only formed when the metal arrives, and so it is not possible to force most of the gas out the vents ahead of the metal flow - it will mostly be captured in the part as porosity. All lubricants give off some gas when heated to the temperature of the molten metal - the amount and type of gas will vary from lubricant to lubricant.

Die Casting Porosity Caused By Lubricant 1

Die Casting Porosity Caused By Lubricant 2

The biggest single lubricant source of gas porosity is the plunger lubricant. The usual problem is that the lubricant is applied ahead of the plunger much heavier than is needed. This is especially true when a dragging or worn tip is nursed along with extra lubricant - this is bad practice and causes the porosity to come and go as the lubricant is increased or decreased. The best option is to use a tip design that provides good life – Poor tip life equals excessive plunger lubricant.

Die Casting Porosity Caused By Lubricant 3

Die Casting Porosity Causes 6Die Casting Porosity Causes 5

 

Gas Porosity (Lubricant) – Key Check Points

Check list of actions for gas porosity from lubricants:

  • Check the amount of plunger lubricant
  • Reduce the die spray lubricant
  • Look for pockets where the lubricant can accumulate on a cold die
  • Check for leaking water lines
  • Check for dripping sprayers
  • Check for leaking hydraulic cylinders

Gas Porosity - Blisters

Gas Porosity Caused by Blisters

Blisters are another version of gas porosity, the gas just happens to be just under the surface. The trapped gas is under high pressure at the end of fill and the metal may shrink and squeeze it more. When the casting is taken out of the die, and the die surface is no longer there to hold the casting shape the skin is soft at the temperature of the casting at ejection, and the trapped gas is able to push up a blister.

Die Casting Porosity, Blister Causes

Blisters – Key Check Points

The same corrections used for gas porosity apply for blisters:

  • Reduce trapped air (see gas porosity corrections)
  • Reduce spray and plunger lubricant
  • Eliminate water on the die
  • Correct venting and vacuum problems

Blisters should be eliminated by correcting the gas porosity problem. Cool the die in the immediate area where the blisters occur by:

  • Cooling the blister area with die spray
  • Cooling the blister area by adjusting water lines
  • Cooling the whole die by slowing the cycle time

Alternative solution is by immediately quenching the casting, which strengthens the skin of the casting.

Shrink Porosity

Die Casting Shrink Porosity

Develops because the metal occupies less space when solid than it did when it was liquid. Happens to all metals (except a few special alloys). For die casting alloys, the difference in volume will be about 4% to 6%. This extra space will be concentrated at the last point to solidify, which is the hottest spot in that section of the casting.

Shrink porosity is rough and irregular in shape and this shape characteristic is the quickest and easiest way to identify shrink porosity. The shape and appearance of the porosity comes from the way the casting solidifies. This solidification process is important to understand if you are going to diagnose shrink defect problems, so we will spend a few minutes reviewing it. 

Die Casting Porosity, Shrinkage

When the casting is filled, it is filled with high velocity metal that is very turbulent, and is likely to be a spray. As the casting solidifies towards the center (or other hot area), the solidification rate slows down, and a dendritic structure starts to appear. Dendrites are crystal structures from the pure base metal (aluminum, magnesium or zinc) - they are tree like structures that form in the solidifying liquid. 

Die Casting Porosity, Shrinkage Causes

The dendrites grow slowly, and by the time the last metal solidifies, there will be a lot of dendrites in this area. This structure will predominate at the last point to solidify, and the rough dendritic structure causes shrink porosity holes to have a rough surface. This roughness is a guide to the cause of the porosity. The shrink porosity is usually crack like in appearance, and is jagged, rough and irregular in general.

Die Casting Porosity, Shrinkage Causes 2 

When the casting is filled, it is filled with high velocity metal that is very turbulent, and is likely to be a spray. This turbulence will cause the surface (where the die is very cold compared to the hot metal) to freeze first. The skin freezes very quickly, which forms a very strong, dense, and fine grained surface with very low porosity, this is due to the rapid freeze rate. Once the skin has formed, the freeze rate slows down and the composition gradually changes.

We'll continue next week with more about porosity caused by shrinkage and the conclusion of the presenation


What is die casting porosity? 

Gas porosity is the biggest single problem in die casting. The high gas content prevents heat treating or welding because it makes the strength unpredictable. Gas porosity is round and generally smooth, although it can be flattened to some extent by pressure. The actions taken to reduce gas porosity in general are not the same as the actions for reducing shrink porosity.


Die Casting Process in Google and NADCA News:

NADCA Program - Use Your Data to Develop Value Streams

NADCA Video News - Video News: NADCA Research Update - On-Demand Melting


Hill and Griffith Customer Service

We're known for our hands-on approach. Let us visit your plant, offer die casting technical support and recommend release agents, lubricants, plunger lubricants and permanent mold lubricants that suit your needs. Products that represent the latest in technology and ongoing research that enhance competitiveness and increase productivity. 

Hill and Griffith Samples

Product Samples

We are pleased to provide samples in quantities large enough to allow you to "try before you buy." Die Casting and Squeeze Lubricants- Diluco®, Permanent Mold Coatings- Concote™, Plunger Lube™- Graphite and non-graphite oils and pastes with excellent anti-wear properties, Casting Operations Products: Start-up lubes, Ladle coatings, Anti-soldering pastes, Water glycol, Trim press lubricants, Surface protection for casting storage, Corrosion protection for die storage, Cleaners for machines and dies, Corrosion protection for machines, Heat treatment quenchants, and Heat-transfer fluids. Also, Industrial Lubricants Griflube®, Hydraulic fluids with fire-resistant and anti-wear properties, Bio-Syn natural ester-based hydraulic fluid, Way oil knuckle lubes and Metalworking Fluids- Grifcut™

Contact us for Product Samples

Hill and Griffith Customer Service

Technical Services & Support

On-site process surveys, Casting defect investigations, Product testing, Tooling start-ups and Statistical process controls and much more. Also, lab facilities are available to provide testing upon request. 

Contact us to Arrange a Visit

Bulletins and Technical Papers for Die Casting Products

Tags: Die Casting, diecasting, die casting lubricant, Die Casting Porosity

Subscribe to Die Casting News

Die Casting News

Follow Me

Diecasting News Categories

see all