Posted by Hill and Griffith Company on Aug 23, 2017 1:45:28 PM

NADCA EC-515 Die Casting Defects Course Review, Basics for controlling die casting defects - By Dr. Steve Midson

  • Reduce Die Casting Cracks, or tears, or hot cracks have many causes, but usually are at least partially caused by shrinkage cracks on the surface
  • Most often, the casting is stretched in the die as it cools because the die doesn’t change dimensions while the casting is cooling and contracting. The stretching causes cracks at the weak point (the last point to solidify)

Die-Casting-Crack-Prevention-1.jpg

  • Shrinkage cracks on the surface occur during solidification, and have a dark surface - cool the corners or heat up the adjacent areas, add radii to the corners for this type of crack
  • For castings that crack while cooling in the die, the crack will also be at a hot spot – increase radii
  • Mechanical stress can cause cracks when the die opens or the casting ejects (or during slide operations)
  • Cracks at the base of long cores or fins, dragging or sticking of projections into one die half may indicate die shift when the dies separate
  • The factors in die alignment should be checked, such as: die “droop” (no die carrier), worn guide pins, worn linkage, worn tie bar bushings, worn shoes under the moving platen, uneven tie bar stress, etc.
  • The cracks at ejection are usually accompanied by drag marks of some sort.
  • Check the ejector plate for worn bushings, be sure the ejector plate operates straight. Look for undercuts from erosion in the die that cause the casting to hang up

Die-Casting-Crack-Prevention-2.jpg

(Thanks to All About Metallurgy for posting this PDF. We'll cover other aspects of die casting defect control by the proper use of die casting lubricants from the course in upcoming blog posts)

(If you liked this article you might also like this post on, "Die Casting Defects")


Hill and Griffith Customer Service

We're known for our hands on approach. Let us visit your plant and recommend release agents, lubricants, plunger lubricants and permanent mold lubricants that suit your needs. Products that represent the latest in technology and ongoing research that enhance competitiveness and increase productivity. 

Hill and Griffith Samples

Product Samples

We are pleased to provide samples in quantities large enough to allow you to "try before you buy." Die Casting and Squeeze Lubricants- Diluco®, Permanent Mold Coatings- Concote™, Plunger Lube™- Graphite and non-graphite oils and pastes with excellent anti-wear properties, Casting Operations Products: Start-up lubes, Ladle coatings, Anti-soldering pastes, Water glycol, Trim press lubricants, Surface protection for casting storage, Corrosion protection for die storage, Cleaners for machines and dies, Corrosion protection for machines, Heat treatment quenchants, and Heat-transfer fluids. Also, Industrial Lubricants Griflube®, Hydraulic fluids with fire-resistant and anti-wear properties, Bio-Syn natural ester-based hydraulic fluid, Way oil knuckle lubes and Metalworking Fluids- Grifcut™

Contact us for Product Samples

Hill and Griffith Customer Service

Technical Services & Support

On-site process surveys, Casting defect investigations, Product testing, Tooling start-ups and Statistical process controls and much more. Also, lab facilities are available to provide testing upon request. 

Contact us to Arrange a Visit

Bulletins and Technical Papers for Die Casting Products

Tags: Die Casting, Metal Casting, Aluminum Die Casting Process, Die Casting Release Agent, Die Casting Defects

Subscribe to Die Casting News

Die Casting News

Follow Me

Diecasting News Categories

see all