Controlling the quality of raw materials, additives is critical to high-quality green sand system ferrous castings
Basic understanding of raw materials is equally important as good quality control measures and consistent operating practice.
Controlling raw materials is critical to the success of iron casting production. The base silica sand is often overlooked, with the main focus on bentonite additions. Carbonaceous additives can be considered a “necessary evil” to ensure a good surface finish and reduction in sand-related surface defects. Other additives are used when systems get out of balance, and these will further complicate the complexity of green sand systems.
For castings requiring cores this becomes a bigger issue, as many differing resin systems are employed for core production, and these must be taken into consideration when controlling both the carbonaceous levels and the overall grading of the sand system. The twin effects on additional carbon and loss-on-ignition, and overall sand grading, need careful understanding and control.
(This week's post is from Foundry Management and Technology Feb 19, 2009 by Alexander Brown)
Control of raw materials
Much has been documented about additives to green sand methods. What follows here is a discussion of the need for a complete understanding of the sand system, so that operators can make judgments based on fact. Of the many systems I have observed worldwide, most share many common features that give cause for concern. This is not because the operators do not have the means to control the system, but because their decisions are based on a lack of validated data. Some of my concerns are:
• Poor sampling;
• Frequency and timing of samples;
• Lack of calibrated testing;
• Focus on the wrong control areas;
• Lack of understanding of primary and secondary sand tests;
• Little focus on silica sand or sand grading;
• Bentonite emphasizes detriment to carbonaceous additive;
• Poor in-coming test procedures;
• Over-reliance on suppliers.
All of these are important, but equally good castings can be produced from systems with little or no control. By control, I mean a basic understanding of all the raw materials used together with in-house testing and/or approved certification, coupled with good, consistent casting practices. This is measured by general scrap rates and the costs associated with knockout and shot blasting, costs so often not taken into consideration when selecting the raw materials to be used in the system.
Mass balance checklist
1. Return-sand storage silo/bunker capacity
2. Return-sand temperature/moisture (at various points)
3. Weight of sand on line/in boxes etc
4. Core weight input (if applicable)
5. Fines extraction/Sand losses
6. Additive control/weigh calibration/stock against usage
7. Sand carryover at knockout
8. Shot blasting times/consumption
9. Scrap levels/sand related defects
10. Sand to metal ratio/casting weight data
11. Volatiles data at mill and in return sand
12. Loss-on-ignition data at mill and in return sand.
A great deal of information can be gathered from doing a complete mass balance on a system. This exercise picks up so much useful data that it should be a regular exercise in all foundries, especially if the casting weights or size of castings alters over time. Consider the simple question “What is the total sand weight?” Normally, this is met either with a wild estimate or a complete blank response.
From the data gathered a much clearer picture may emerge. Most important, we know that control systems can actually monitor the burn-out rates of bentonite and carbonaceous additives. Most observers agree that additions at the muller require time to be effective, and by understanding how the sand reacts to varying sand-to-metal ratios, proactive steps can be taken. Various foundries have used predictive software or even a simple traffic light system to monitor heat demand, with good results. It is not the actual system that matters, but, importantly, understanding what is happening and being one step ahead of it.
Those foundries producing castings without cores are obviously in a much better position than those with cored products. Core systems simply have to accept coarser sand as a dilution, but with careful selection this does not have to be a problem. More important is knowing the AFS (Average Fineness Number) and AGS (Average Grain Size), and determining what produces the best casting surface at the most economical cost. The AFS clay-grade washing and sieving of the washed sand needs regular review, and these tests, along with optimum additive rates, are the keys to success in a green sand system.
Bond suppliers will claim many advantages for their products, but many differing bentonites are used with success throughout the iron-casting world. That said, consistency is the main aspect to control, and that is another matter entirely. Few foundries have the specialized equipment needed for incoming control, so testing should be limited to meaningful values and working with your supplier will establish a working specification. A smooth surface, free from defects is the standard for excellent casting surface finish.
Many coal products are available, with many claims. Coal, either as high-quality bituminous or lower-grade material, is the main additive, and grading selection should also be tailored to the castings being produced. Coal is by far the cheapest and safest carbonaceous additive to systems. Its unique, all-around properties make it easy to use; its use is so underrated that in most cases it is under-used, and most systems do not benefit fully from its various beneficial properties.
Most other carbon additives are highly volatile products normally added to poorer quality coals to enhance the level of volatile content. These can cause additional problems in high concentrations due to hydrogen/nitrogen gases, and are quickly eliminated from a system without contributing to the coke build-up (total carbon). This can be an expensive approach to adding carbonaceous additives, and too often the operator has no idea what products he/ she is using, as the blends are often “trade secrets.” To understand a system and its interaction with additives you simply have to know what you are adding, and why. The classic system of using one, single-source bentonite and coal is by far the simplest and most cost-effective route to producing quality castings.
Mixer controls, technical support
The need for control in this area is obvious as changes here are reflected throughout the system. Regular mixer maintenance coupled with calibration of additives and usage checks against actual stock purchases often may spot problems before they give concern. This should be part of the mass balance procedure that should be a routine feature.
Getting the primary and secondary testing balance right is difficult for foundries. Too much, and the testers see no positive advantages other than routine test control. Too little, and there is no starting point for investigation and correction once things go wrong.
Concentrate on the primary tests to ensure consistency. Especially during periods of good casting performance, take time to monitor what makes the system work. Look to the secondary tests to reinforce the casting quality, and test only if you are prepared to react on the results. Meaningless testing is a waste of resources. Ensure proper reporting and graphing of data. Ultimately, all sand testing shows a “trend.” Even if the testing methods are not perfect, if conducted on a consistent basis they will show the trend line to which you are able to react.
Bentonite testing has been well documented. One area for control is a foundry’s raw-material acceptance testing. This can be established in conjunction with the supplier, and simple tests such as swelling ability, sieve grading, and specific gravity are useful in association with active clay calibrations.
One of the most difficult tests from which to get consistent results is the volatiles test, and yet many foundries use this as the guide for carbonaceous additions irrespective of the casting quality. With 3 or 4 decimal place measurement and a weight loss at a specified temperate (910ºC) and time (7 minutes) on a small sample weight (1 or 2 grams), it can be a difficult test, especially between different laboratories. This volatiles test is normally used in conjunction with the loss-onignition test and investigations into an alternative method to supplement these tests will ensure focus on this critical area for consistent casting performance.
Total carbon testing
For example, Lincoln Castings Ltd. began to use this control method on its LM1 and LM2 molding lines, starting around 2001. It was introduced as a routine test for their straight coal/ clay system. Over the following year it became obvious that the interaction of total carbon, sulfur, volatiles, and loss-on-ignition was critical to the quality of the castings.
The radar graph shown to the left was used to monitor the relationship, and it was proved that if the total carbon, losson- ignition, and volatiles were kept in the desired ranges, the casting performance was acceptable. If any of the results fell into the grey area (the area of concern) then positive action had to be taken. Equally, going out of the maximum area also required reduction of additives. Sulfur levels normally mirrored the total carbon and ran in the range 0.06 to 0.09.
A testing unit used at Lincoln Castings Ltd. was supplied by Leco UK — a SC144 carbon/sulfur machine. It was selected because it determines carbon/sulfur in various organic matrices from low concentrations (e.g., bentonite) to high levels, such as coal and coke, as well as higher carbon products, such as recarburizers and graphites. This instrument offers a simple solution that determines carbon and sulfur simultaneously using direct combustion and infrared detection.
No hazardous chemicals are used and accurate results are provided in 3 minutes from a small sample weight of 0.3 grams, using reusable refractory sample boats, without accelerating elements. Coupled to the unit is an automatic weighing unit with a dedicated software package, allowing for data storage, statistical analysis and customized operating parameters.
The samples (such as bentonite, coal, silica sand, as well as system and return sand and extraction fines) are tested on a daily basis to ensure proactive steps can be taken, coupled with the routine sand testing. Analysis begins with a nominal weight of 0.3 grams being weighed in a combustion boat. The sample is placed in a pure-oxygen environment regulated at 1,350ºC. The combination of high temperature and oxygen flow cause the sample to combust, and to go through an oxidation and reduction process that causes carbon and sulfur bearing compounds to break down and free the carbon and sulfur. The carbon then oxidizes to form CO2 and the sulfur forms SO2.
The combustion system allows the sample gases to remain in the high-temperature zone, and this permits efficient oxidation. Gases flow through two anhydrone moisture traps and into the infrared detection zone. Then, the carbon and sulfur dioxide values are converted, taking into account the sample weight, calibration, and known moisture value.
The SC 144 can be classed as high-end, multi-element detection instrument, and various laboratories worldwide were checked to determine the effects of alternative units. Many labs have older carbon and carbon/sulfur units, doing mostly metal analysis. It was decided to check samples on both an SC 144 and a CS 244 to determine the difference in results based on a wide range of samples.
The CS 244 and other units in the CS series are ideal for smaller, lower-volume laboratories looking for a cost-effective solution, without sacrificing precision, reliability, or accuracy. These CS units use induction heating elements and a larger sample weight of 1 gram. Also used are accelerating elements, such as high-purity iron, tungsten, or copper with a temperature in excess of 2,000ºC for 15 seconds, to ensure complete combustion. Any CO or SO3 is converted to ensure that only CO2 and SO2 are measured. Both of these gases absorb infrared energy at precise wavelengths within the spectrum. Energy is absorbed as the gases pass through the infrared absorption cells.
The CS unit uses a refractory crucible, and a lid is recommended to prevent any of the sample being removed by the pressure blast of oxygen used in this unit. Research that compared their performances showed the CS cannot measure the initial fast release of volatile gas and therefore the total carbon readings are around 1% lower than when using the SC unit.
Both units are calibrated using a calcium carbonate at 12% carbon and 0.0106% for sulfur. Calibration graphs and running widely varying samples show the units are very accurate, with excellent reproducibility.
As a control measure, many foundries have relied on loss-on-ignition and volatiles tests to measure carbonaceous addition. Coupled with AFS clay grade and active clay measurement, this was considered adequate testing, along with the usual series of permeability, strength, and moisture tests. Experience has shown that active clay levels in most systems range from 1% to 2% higher than required, and these levels are regarded as a safety feature. Whereas we know foundry workers make excellent moldable sand, this does not always translate into top quality castings.
Volatiles testing can be difficult and total carbon determination removes the need for total reliance on this method. A common problem with volatiles testing is the use of a wideneck crucible with a poor fitting lid. These units always give a larger false reading and the use of the standard parallel-sided crucible is urged, with a tight fitting lid. Loss-on-ignition is of course an easier test and this can be backed up with further testing on washed and unwashed sand samples. Conduct both volatiles and loss-on-ignition tests before and after washing out the clay grade, to determine the contribution from the carbonaceous additive. Approximately 1% of volatiles in a sand system actually comes from the bentonite addition.
One foundry does not have all the answers, so it was important to collect sand samples from as wide a group as possible, By selecting samples from foundries Malaysia, Thailand, Czech Republic, Denmark, South Africa, India, as well as the U.K., it was possible to include all available core binders and also differing silica sands, bentonites, and carbonaceous additives, including those containing lustrous carbon.
All participating foundries were assessed for optimum use of raw materials, control of sand testing, and molding properties, to ensure a level playing field. If the locations met the criteria, sand samples were collected over a period of time (all through 2005) to look at trends and importantly at casting performance.
The key measurables were casting scrap related to sand condition, surface-finish quality, sand carryover at knockout, and shotblast times. Of course, not all of this can be attributed to carbonaceous additive but in the end I settled on a good, average, and poor ratings. This may at first seem too simple to be useful, but I believe the results and conclusions justify the selection. Now, further work needs to be done to put numbers against the various selected categories.
Having defined the foundry, samples were collected over the year, and washed and unwashed samples were tested for volatiles and loss-on-ignition, as well as using the SC 144 unit to determine the total carbon and sulfur levels. I personally visited each foundry, in order to monitor casting performance and to crosscheck our own laboratory results. It soon became apparent that the categories matched the level of total carbon within bandwidths.
As no database of information was available, over 20 foundries were tested with total carbon levels ranging from a low 1.5% to a high of 6.68%. Out of interest, and because the SC 144 also measures sulphur at the same time, we recorded the numbers and found a range from 0.045% to 0.13%. Against each sample we conducted volatiles and loss-on-ignition tests to see if there was a relationship, and to check the foundries’ own results (which in itself was a useful exercise): quite differing results were obtained. Three independent laboratories were used, including foundries and suppliers, to verify results over the year. The table shows the results from a single session using various samples on the SC 144 unit, from low- to high-carbon content. The CS results show the difference in the detection systems, but the accuracy shows the possibilities and the versatility of the units for rapid testing and control.
The main list shows the results from the average of samples taken from each foundry’s system sand. Both volatiles and loss-on-ignition tests were carried out, too, to supplement the total carbon results. All these results come from the SC 144 unit, so we may be confident we have measured the total carbon content.
Evaluating volatiles, loss-on-ignition properties (page 3)
The whole matter of the use of carbonaceous additives and their purpose has been well documented. This work simply adds to the conclusion that there is an interaction between the total carbon in a sand system, allied to a level of active effective volatiles, and a loss-on-ignition maximum for successful casting production. Often overlooked in problem solving is the amount of volatiles, which must come from the bentonite, and typically this is classified as 10% of the AFS clay grade. To investigate this further, washed and unwashed tests reveal the true active volatiles content from the carbonaceous additive. Many foundries are simply unwilling to move their loss-on-ignition numbers above 5%, which limits the active volatiles, which in turn limits casting performance.
The graph shows the approximate levels of volatiles for good casting performance from results obtained in one foundry. Each foundry could construct its own graph based on the parameters selected. Obviously other factors come into play but it is clear that the quality active volatiles release is one of the major factors for casting excellence. The “classic” loss-on-ignition (LoI) to volatiles ratio of 3:1 still holds true in most cases, and when further linked to total carbon levels the picture becomes clearer.
Clay-grade LoI is the difference between the washed and unwashed LoI tests. Adding this difference to total carbon will produce the total LoI. Importantly, it shows the correlation between the tests. The example listed shows a clean sand system lacking active volatiles and low in total LoI.
Other control methods
The Mass Balance predictive method is used to ensure heat losses after casting (burn out) are reacted to before pouring, and to ensure that additional additives are added or decreased ahead of heavier or lighter castings. This method finds favor in well organized foundries that control additive levels effectively. It allows for lower levels to be added as normal and larger additions ahead of the heavier casting load. This depends on the sand-to-metal ratio, but with all foundries aiming for maximum efficiency it makes good sense to understand how the system will react to pattern changes and varying heat loads.
This system can be incorporated into the sand plant computer controls, and can equally be used for manual adjustments, using what some foundries call the “traffic light” system. They use red to indicate the heaviest castings on the program, amber for mid-range products, and green for lighter heat loads on the system. Irrespective of the system, the important aspect is to be aware of the system, the heat loads proposed, and to be able to take action before corrective measures are required. Rushed changes based on “feel” may work, but informed change is the safer, more positive approach.
Return sand control is one of the most neglected operating practices in green sand foundries. For most foundry workers, what happens to sand after casting is a mystery. What manages to stay in the system simply re-appears for mulling, and so it goes on. Here is a massive area of potential savings, coupled with the knowledge that a well-prepared return sand will be lower in temperature, higher in moisture (ideally at 2%+), and better developed in terms of bentonite and general condition.
A well-developed return sand is much easier to re-mull. In fact, lower addition levels will be required, which in turn leads to lower moisture in the system sand. With lower moisture levels the conditions for a reducing atmosphere are better and, coupled with adequate carbon levels and active volatile content, this will ensure better performance and result in improved casting quality
Casting knockout is another standard operating practice that often is overlooked as an area of potential quality control. The results of all calculations and control are available simply by looking critically at the resultant castings. The sand peel from the castings, the amount of sand carried over, and the color of the castings is often a good early indicator of casting quality.
Simple, complex, effective
Green sand systems can be simple and complex — simple in terms of additives and control; complex in the amount of variables possible and the need for constant vigilance — but they are simply the most cost-effective method for high volume production of iron castings.
The research shows that total carbon can be a very useful measuring and control tool for green sand systems, coupled with accurate volatile and loss-on-ignition tests. Without exception the foundries categorized as acceptable in this research had total carbon figures in excess of 3%. In foundries categorized as good, it was no coincident that the volatile and losson- ignition figures were also in what the author describes as “a good area.”
Foundries would do better to arm themselves with meaningful data regarding carbonaceous additives. Total carbon determination could include all aspects of a sand system, including raw materials, and this would simplify decision-making. Areas such as return sand and fines extraction could be monitored easily with better control.
All sand systems have differing moisture sensitivity. Using bentonite from known, approved sources coupled with correctly graded coal, with low ash content (less than 3%), ensures the coal does not compete with the bentonite for available water. The key for foundries is to understand the properties of raw materials they use, and to control the consistency. Once this has been established, it will be possible to rely on a minimum amount of additives to achieve the goal of consistent quality castings. Ensuring adequate carbonaceous levels is not difficult but for many foundries it remains only a secondary focus. World-class performance is being demanded by casting buyers, and successful suppliers will need to ensure they operate “in the correct zone,” with effective knownsource additives.
Alexander Brown, FICME, is an associate of James Durrans & Sons Ltd., a global supplier of recarburizers, refractory coatings, coal, coal/carbon/bentonite blends, synthetic and natural graphites, and similar products. This report is based on his research, which earned the British Foundry Medal and Prize for 2008. Contact him at firstname.lastname@example.org
Hill and Griffith Customer Service
The Hill and Griffith Company's green sand metalcasting foundry supplies help achieve the EPA's M.A.C.T. standards and reduce Benzene emissions. Our variety of environmentally sound release agents, coatings, partings, lubricants, core oils and specialty products will help you meet your metal casting's needs. We're known for our hands on approach. Let us visit your plant and recommend products that suit your needs.
We are pleased to provide samples in quantities large enough to allow you to "try before you buy."
Contact Us »
Technical Services & Support
On-site casting defect investigations, product testing, machine start-ups and much more. Also, lab facilities are available to provide testing upon request.